Long-Lifetime Ag/AgCl Electrodes Prepared by Pulse Current Electrodeposition for Chloride Monitoring in the Concrete Environment.

Lifetimes of Ag/AgCl electrodes determine whether it is possible to monitor the concentration of chloride ions in marine concrete structures. A novel manufacturing method, pulse current electrodeposition at a low current density, was proposed to prepare the long-lifetime Ag/AgCl electrode. Influences of electrodeposition duration were investigated on the Nernst response, exchange current density, and lifetime of Ag/AgCl electrodes, and the properties were also compared to those of the ones electrodeposited by applying constant currents. Ag/AgCl electrodes prepared with the pulse current exhibited a wider potential response, a higher exchange current density, and a longer lifetime than those prepared by the constant current under the same equivalent charge transfer conditions. AgCl film on the electrode prepared with the pulse current displayed a thicker layer, a lower density of micropores, a higher Cl/O ratio, and a lower Ag/Cl ratio than those of its counterpart electrodeposited by applying the constant current. The lifetime of the Ag/AgCl electrode was mainly determined by the thickness of AgCl films in the concrete environment. The lifetimes of the Ag/AgCl electrode, which was prepared with a 0.1 mA cm