Welding Technology and Heat Treatment Butt-Welded Joints of Thin-Walled Inconel 718 Alloy Tubes.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
Abstract
The subject of this research was the development of technology for welding and the heat treatment of butt-welded joints of thin-walled Inconel 718 alloy tubes, a process based on orbital TIG welding without a filler metal. The developed technology allows favorable conditions to obtain the appropriate hardness and mechanical properties in the weld area required by AMS 5589. In the tests, the microstructure and mechanical properties were evaluated. Compliance with the requirements was evaluated on the basis of metallographic and mechanical properties tests. The results obtained indicate that the weakest area of the joint is the base material of the thin-walled tube. The welded joints reveal elongation above 10% and tensile strength above 1400 MPa despite the dendritic structure of the weld. In the area of the welded joint, the occurrence of precipitates of the γ' phase and mainly niobium carbide was revealed.