Chemical Stability and Leaching Behavior of ECO EPDM in Acidic Fuel Cell-like Conditions.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
This study investigates the chemical stability and leaching behavior of two environmentally sustainable EPDM elastomers filled with circular carbon black (CCB) and recycled carbon black (RCB) when exposed to acidic, fuel cell-like environments. Accelerated aging tests were conducted in sulfuric acid solutions of varying concentrations (1 M, 0.1 M, and 0.001 M) at 90 °C for 1000 h to simulate long-term degradation in proton exchange membrane fuel cell (PEMFC) sealing applications. Complementary hot water extraction tests (HWET) were performed at 80 °C for up to 168 h to evaluate ionic leaching via conductivity measurements. HPLC-DAD analysis was used to assess organic leachates, while surface changes were examined by SEM and thermal transitions by DSC. Results revealed lower leaching and improved surface preservation in the CCB-filled EPDM, which remained below the critical 5 µS/cm ionic conductivity threshold for longer durations than its RCB counterpart. HPLC results showed filler-dependent trends in organic compound release, with CCB EPDM exhibiting higher leaching only under strong acid exposure. SEM confirmed greater surface damage and porosity in RCB EPDM. Overall, both materials demonstrated adequate chemical resistance, but the CCB formulation exhibited superior long-term stability, supporting its use in sustainable PEMFC sealing applications.