Multi-Parametric Study on Flexural Behavior of Wool-Flax Hybrid Composites Under Thermal Conditions.

The increasing demand for sustainable materials has intensified the interest in natural fiber-reinforced composites (NFRCs) as environmentally friendly alternatives to synthetic composites. However, NFRCs often face limitations in thermal stability, restricting their use in high-temperature environments. To address this, the present study explores the hybridization of cellulosic flax fibers with protein-based wool fibers to improve thermal stability without compromising mechanical integrity. Wool-flax hybrid composites were fabricated using a bio-based epoxy resin through a resin infusion technique with different fiber proportions. The flexural properties of these composites were evaluated under varying temperature conditions to assess the influence of fiber composition and thermal conditions. This study specifically examined the impact of wool fiber content on the flexural performance of the composites under thermal conditions, including behavior near and above the matrix's glass transition temperature. The results showed that the flexural properties of the hybrid biocomposites were significantly affected by temperature. Compared with specimens tested at room temperature, the flexural modulus of all variants decreased by 85-94%, while the flexural strength declined by 79-85% at 120 °C, depending on the variant. The composite variant with a higher wool content (variant 3W) exhibited enhanced flexural performance, demonstrating an average of 15% greater flexural strength than other variants at 60 °C and 5% higher at 120 °C. These findings suggest that incorporating wool fibers into flax-based composites can effectively improve thermal stability while maintaining flexural properties, supporting the development of sustainable biocomposites for structural applications.