ArticleJournal of the mechanical behavior of biomedical materials2025
Toughness measures in solid-state composites of ultra-high molecular weight polyethylene.
Article in Journal of the mechanical behavior of biomedical materials, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
Abstract
Solid-state composites of ultra-high molecular weight polyethylene (UHMWPE) are increasingly being investigated for various therapeutic and sensing use cases in arthroplasty. Due to its extremely high melt viscosity, composites of UHMWPE exhibit a much more distinct phase segregation than lower-viscosity polymer composites. This phase segregation may influence UHMWPE behavior in a different way than microstructural factors studied previously (e.g. crosslinking). The purpose of this study was to quantify UHMWPE nanocomposites' resistance to failure via several distinct measures, across a range of carbon black (CB) filler loadings. Results showed that tensile and impact toughness followed similar trends: both maintained or increased in magnitude over neat controls at low filler concentration, then decreased at higher filler contents. On the other hand, fatigue crack propagation resistance (CPR) demonstrated similar behavior to tensile and impact toughness at lower concentrations but diverged at higher concentrations. From 2.5 wt% CB to the highest concentration tested (10 wt% CB), fatigue properties improved-unlike tensile or impact toughness. The observed transitions in macroscopic behavior with increasing filler content coincided with microstructural phenomena observed via scanning electron microscopy (SEM) and fracture surface imaging. These phenomena included a transition from transgranular fracture to intergranular fracture, the onset of complete granule coating, and the formation of intergranular voids. This work demonstrates that tensile and impact toughness are not necessarily indicative of fatigue CPR in these materials. Broadly, the findings presented in this study motivate further investigation of structure-property relationships for phase-segregated polymer composites and demonstrate promise for their use in high-load scenarios.