Considering the bonding shear strength and flexural performance of bamboo scrimber bonded with magnesium oxysulfates adhesives of different properties.
Article in Scientific reports, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
Abstract
To investigate the effects of magnesium oxysulfates adhesives with varying performance characteristics on the shear strength and bending resistance of bonded bamboo, eight types of these adhesives were prepared and applied to bamboo specimens of size 2150 mm × 22 mm × 5.5 mm for testing. The flowability, flexural strength, and compressive strength of the adhesives were measured to analyze their impact on the performance of bonded bamboo. The experimental results showed that the magnesium oxysulfates adhesive with the number H exhibited the highest adhesive shear strength under 7-day and 28 day curing conditions, at 1.05 MPa and 1.46 MPa, respectively, while the adhesive with the numbers B and A had lower strength. Magnesium oxysulfates adhesives with varying performance characteristics also had a significant impact on the bending resistance of glued bamboo. The adhesive with the number H showed the highest bending strength at 79.02 MPa under 28 day curing conditions, while the adhesive with the number B had the lowest bending strength at 39.96 MPa. The study also found that the thickness of bamboo curtains had a relatively small effect on the bending resistance of magnesium oxysulfates cementitious materials, but temperature and water immersion conditions had significant impacts on the mechanical properties of magnesium oxysulfates adhesives. After treatment at 250 °C, the peak load of magnesium oxysulfates adhesive significantly decreased, showing more pronounced performance degradation. After one year of immersion in clean water, the bending strength of magnesium oxysulfates adhesive decreased from 69 to 58 MPa, and the softening coefficient decreased from 1.0 to 0.79. From this, magnesium oxysulfates adhesivess with varying performance characteristics have significant impacts on the adhesive shear strength and bending resistance of glued bamboo. By optimizing the formula and process of magnesium oxysulfates adhesive, its application performance in glued bamboo can be significantly improved, providing scientific basis and technical support for promoting the widespread application of bamboo in construction and engineering fields.