Effect of Combined Equal-Channel Angular Pressing and Rolling on the Microstructure and Mechanical Properties of Zn-0.5Ag-0.2Mg Alloy.
Article in Materials (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
Zn-Ag alloys are deemed extremely promising materials for manufacturing biodegradable medical implants. Nonetheless, their practical applications are still constrained by inferior mechanical properties. To tackle this issue, Zn-0.5Ag alloy was alloyed with Mg (0.2 wt.%) and processed by combined equal-channel angular pressing (ECAP) and rolling, with different rolling reductions (40%, 60%, and 75%). ECAP-processed Zn-0.5Ag-0.2Mg alloy exhibited superior mechanical properties to its as-cast counterpart. Subsequent rolling of 40% further enhances the mechanical performance of ECAP-processed Zn-0.5Ag-0.2Mg alloy, with yield strength (YS), ultimate tensile strength (UTS), and elongation (EL) reaching 255 MPa, 309 MPa, and 52%, respectively, surpassing the application requirements. As the rolling reduction increased to 60% and further to 75%, YS and UTS declined, whereas EL rose continuously. The underlying mechanisms for the variation in strength and ductility were elucidated based on microstructure evolution analysis through optical microscopy (OM), scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) characterizations.