Synthesis of Crosslinkable Alkali-Soluble Resins and Self-Crosslinking Polyacrylic Latexes.
Article in Molecules (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- AAEM/ADH Self-Crosslinking Waterborne Polyurethane-Acrylate Binder for High-Adhesion Waterborne Inks on PET Films.Polymers · 2026Article
- Waterborne Random Copolymers as Polymeric Surfactants for Emulsion Polymerization.Industrial & engineering chemistry research · 2026Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
In the field of water-based inks, the use of alkali-soluble resins (ASRs) as polymeric surfactants for synthesizing polyacrylate latexes has become a mainstream method. This study first designed and prepared crosslinkable ASRs with a diacetone acrylamide (DAAM) crosslinking monomer via emulsion polymerization. These ASRs were then employed as surfactants to synthesize self-crosslinking polyacrylate latexes through an in situ one-pot method, systematically investigating the influence of crosslinkable ASRs on the properties of the corresponding polyacrylate latexes. The research revealed that all prepared polyacrylate latexes exhibited a core-shell structure. With increasing DAAM content in the ASRs, the latex particle size gradually increased while the particle size distribution narrowed. All latexes demonstrated excellent stability, with absolute ζ-potential values exceeding 30 mV. The introduction of DAAM into ASRs significantly increased the glass transition temperature in the high-temperature region of the corresponding latex films, with the tensile strength reaching a maximum of 7.96 MPa. Moderate crosslinking in ASRs substantially improved the water resistance of latex films. Crosslinking degree tests indicated that latex films prepared through either single shell-layer crosslinking or single core-layer crosslinking showed relatively low crosslinking degrees, while only the dual core-shell crosslinking strategy could effectively enhance the film crosslinking degree. However, excessively crosslinked shell layers significantly hindered the crosslinking reaction of DAAM in the core layer, leading to reduced overall film crosslinking. Additionally, incorporating a certain number of DAAM crosslinking groups in ASRs was found to improve the adhesion of corresponding water-based inks on PE and BOPP substrates, with adhesion on BOPP substrates reaching up to 100%.