Preparation and Application of Humidity-Adaptive Wooden Artifact Crack Consolidants Based on Lignin-Epoxy Acrylate.

Due to compatibility issues between traditional reinforcing materials and the substrate of museum wooden artifacts, interface failure occurs after crack reinforcement, particularly under dry and wet cycling conditions. This significantly compromises the durability of reinforcement. To resolve this issue, dealkalized lignin was grafted onto epoxy acrylate (LEA) to synthesize a novel consolidant with both humidity responsiveness and mechanical compatibility. The resulting LEA exhibited excellent multilayer adsorption capability and demonstrated synchronous and uniform hygroscopic expansion behavior, closely matching that of archeological wood. DMA revealed that LEA2 has an elastic modulus of 261.58 MPa and a Poisson's ratio of 0.35, comparable to artificially degraded wood, effectively mitigating interface stress caused by rigidity differences. Furthermore, LEA effictively reinforced micron-scale cracks while maintaining the original microstructure of the wooden artifact. This material provides a promising solution to the compatibility challenges of traditional consolidants under humidity fluctuations and offers a new approach for the stable preservation of museum wooden artifacts.