Evaluation of γ-Irradiation Effects on EPDM/SBS Blends for Durability and Recycling Potential.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
This study investigates the stability behavior of blends composed of ethylene-propylene-diene monomer (EPDM) and styrene-butadiene-styrene (SBS), focusing on the effects of γ-irradiation on these materials. FTIR, CL, and DSC analysis indicate that blends with more than 50% SBS demonstrate remarkable resistance to significant radiation doses. This study highlights that at increased γ-irradiation doses, specifically 100 and 150 kGy, structural changes in the polystyrene aromatic rings are detected, providing insights into the modifications induced by radiation exposure. Among the tested formulations, the blend containing 75% SBS demonstrated the best performance against γ-irradiation, showcasing superior mechanical and structural resistance to radiation-induced degradation. The results indicate that γ-irradiation leads to managed degradation within the SBS/EPDM mixtures: while EPDM experiences increased crosslinking, SBS proves resilient against crosslinking, thus bolstering the stability of EPDM under irradiation scenarios. Additionally, thermal analysis underlines the beneficial role of SBS by showing enhanced thermal stability in SBS-rich samples (SBS content higher than 50%) experiencing reduced thermal degradation through repeated heating cycles. This outcome suggests that the inclusion of SBS effectively reduces crosslinking and chain scission impacts, thereby enhancing consistency in thermal properties over multiple cycles.