Force and moment analysis of clear aligners: Impact of material properties and design on premolar rotation.

Objective: To quantitatively analyze and compare the forces and moments generated by thermoformed polyethylene terephthalate glycol (PETG) and direct-printed TC-85 clear aligners (CAs), with various margin designs, during premolar rotation. Methods: In total, 132 CAs were fabricated and divided into four groups (n = 33 per group). Group C consisted of thermoformed PETG aligners with a 2 mm gingival margin. Group E comprised direct-printed TC-85 aligners with equi-gingival margin, whereas Group G utilized direct-printed TC-85 aligners with 2 mm gingival margins. Finally, Group T featured direct-printed TC-85 aligners with an additional 1 mm thickness at the mesial embrasure. The forces and moments were measured using a 6-axis force/moment transducer at 2°, 3°, and 4° of rotation. All measurements were conducted at 37°C to simulate intraoral conditions. Forces were measured in the buccolingual, anteroposterior, and vertical directions, while moments were measured in the mesiodistal, buccolingual, and rotational planes. Results: The PETG aligners (Group C) showed significantly increased buccal and posterior force across the rotation angles ( Conclusions: Direct-printed TC-85 aligners demonstrated superior force consistency and reduced unwanted side effects compared with traditional PETG aligners. Although marginal design modifications did not significantly improve rotational efficiency, they effectively reduced unwanted intrusive forces.