Impact of CuSn10 Powder on Mechanical Properties and Tribological Performance of Novel Basalt Fiber-Reinforced Hybrid Composites.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Hybrid composite materials reinforced with both fibers and particulate fillers are increasingly used in engineering due to their favorable balance of mechanical strength, reduced weight, and enhanced tribological performance. This study investigated the effect of CuSn10 bronze powder additions (5%, 10%, and 15% by weight) on the mechanical and tribological properties of novel basalt fiber-reinforced polymer (BFRP) composites. The composites were fabricated via vacuum-assisted processing and tested under dry sliding conditions with varying loads (10, 20, and 30 N) and sliding speeds (0.1, 0.25, and 0.36 m/s). The results show that the optimal tensile strength (440.6 MPa) was achieved at 10 wt% CuSn10, while the best tribological performance was observed at 15 wt% CuSn10, under a 10 N load and 0.25 m/s sliding speed, where the coefficient of friction decreased by up to 38% and the specific wear rate was reduced by more than 50% compared to the unreinforced BFRP composite. These enhancements are attributed to the formation of a stable oxide-based tribolayer (CuO, SnO
Indexed as
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.