Push out bond strength of resin -based endodontic sealer loaded with silver gold nanoparticles in vitro study.

objectivesThe push-out bond strength to the intraradicular dentin was evaluated in this in vitro study using an epoxy-based endodontic sealer loaded with silver-gold nanoparticles. Additionally, the benefits of using the nanoparticles as a canal pretreatment before applying the sealer were evaluated in comparison to using the sealer alone. METHODOLOGY: After being decoronated and instrumented, thirty extracted human central incisors were obturated and then divided horizontally into three parts (coronal, middle, and apical) with a thickness of 2 mm. Three groups of slices were created at random: Groups I (control) and II received AH Plus sealer, AH Plus sealer loaded with silver gold nanoparticles, and III received nanoparticles as a pretreatment for the canal prior to gutta-percha and AH Plus sealer for obturation. The specimens were loaded at a rate of 0.5 mm/min utilizing a Universal Test Machine and put through a push-out test. Statistics were applied to each data collection. Additionally, the significance level was set at P ≤ 0.05.

resultsA push-out test showed that the groups differed significantly from one another. The tested groups differed significantly in both the coronal and middle portions, with group (II) exhibiting the highest push-out strength values. Group (II) had the highest push-out strength values in the apical portion (3.66 ± 0.72), followed by group (III) (2.90 ± 1.45), while group (I) had the lowest value (2.88 ± 1.73). There was no significant difference between the groups.

conclusionsthe experimental AH Plus sealer combined with silver-gold nanoparticles demonstrated the most effective adhesion followed by nanoparticles as a canal pretreatment prior to sealer application when compared to AH Plus sealer alone.