Analysis of the Damage and Failure Mechanism of Q345 Steel Plate with Initial Defect Under Different Temperature Conditions by Peridynamics.

The high temperature performance of steel structures has long been a focus of research, but research on the damage and crack propagation mechanism of steel with initial defects at high temperature is relatively low. The high temperature performance of most steel structures in engineering has an important impact on the function and safety of the whole structure. At present, Peridynamics (PD) theory uses the integral method that has unique advantages compared with traditional methods to solve structural damage and fracture problems. Therefore, the effect of temperature change on steel properties is introduced into the PD, and the PD constitutive equation at high temperature is proposed. The damage and crack propagation mechanisms of 2D Q345 steel plates with bilateral cracks and different bolt holes at 20 °C, 300 °C, 400 °C and 600 °C were analyzed by applying temperature action and external load to double-cracked steel specimens by the direct thermostructural coupling method. At the same time, the damage values, displacement changes in X direction and Y direction under different temperatures were compared and analyzed, and the effects of temperature, bolt hole and external load on the damage, displacement and crack growth path of different parts of the structure were obtained.