Capacitance and Dielectric Properties of Spin-Coated Silk Fibroin Thin Films for Bioelectronic Capacitors.

Silk fibroin, a biocompatible and flexible biopolymer derived from Bombyx mori silkworms, has shown promise in bioelectronics, due to its adjustable dielectric properties. This study investigates the influence of spin coating parameters on the optical, electrical, and dielectric properties of thin silk fibroin films. Silk fibroin solutions were spin coated onto indium tin oxide (ITO)/glass substrates at speeds ranging from 1000 to 7000 revolutions per minute (RPM), resulting in films with thicknesses that varied from 264.8 nm to 81.9 nm. Atomic force microscopy analysis revealed that the surface roughness remained consistent at approximately 1.5 nm across all the spin coating speeds, while the film thickness decreased with the increasing spin speed. Ultraviolet (UV)-visible spectroscopy showed that the transmittance at 550 nm increased from 81.2% at 1000 RPM to 93.8% at 7000 RPM, and the optical bandgap widened from 3.82 eV at 1000 RPM to 3.92 eV at 7000 RPM, which was attributed to reduced molecular packing and quantum confinement effects. Electrical characterization showed that thinner films (a spin speed of 5000-7000 RPM) exhibited a 15-fold increase in the leakage current, rising from 2.99 pA at 1000 RPM to 44.9 pA at 7000 RPM, and a decrease in resistance from 334 GΩ at 1000 RPM to 22.2 GΩ at 7000 RPM. The capacitance-voltage measurements indicated a 4-fold increase in voltage-dependent capacitance for thinner films, with capacitance values increasing from 36 pF at 1000 RPM to 176 pF at 7000 RPM. Dielectric loss analysis revealed that thinner films experienced higher energy dissipation at low frequencies (tan δ of 0.041 at 0.01 MHz for 7000 RPM), but lower losses at high frequencies (tan δ of 0.123 at 1 MHz for 7000 RPM). These findings emphasize the importance of film thickness control in optimizing the performance of silk fibroin-based bioelectronic devices.