ArticlePolymers2025
Structure-Properties Correlations in Novel Copoly(urethane-imide) Films Selectively Destructed Under Thermolysis and Hydrolysis in Alkaline Media.
Article in Polymers, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
13 authors.
Funding
Abstract
The paper describes changes in the structure, morphology, mechanical and thermal properties of porous film samples of poly(4,4'-oxidiphenylene)pyromellitimide prepared as a result of selective destruction of urethane blocks in copolymers composed of pyromellitimide blocks and polyurethane blocks. The initial samples of the new composition of statistical copoly(urethane-imide)s (CoPUIs) were prepared via polycondensation methods using pyromellitic dianhydride (PMDA), 4,4'-oxidyaniline (ODA), 2,4-toluylenediisocyanate (TDI), as well as polycaprolactone (PCL) and poly(1,6-hexanediol/neopentylglycol-alt-adipic acid) (ALT) as monomers. The molar ratio of imide and polyurethane blocks in CoPUI was 10:1. The initial films were heated up to 170 °C to complete the polycondensation processes, after which they were subjected to thermolysis and hydrolysis. The thermolysis (thermal degradation) of copolymers was carried out by heating the initial samples to temperatures of 300 °C or 350 °C. Then, the thermolized films were subjected to chemical degradation in hydrolytic baths containing an aqueous solution of potassium hydroxide. As a result, urethane blocks were destroyed and removed from the polymer. The resulting products practically did not contain polyurethane links and, in chemical composition, were practically identical to poly(4,4'-oxidiphenylene)pyromellitimide. NMR and IR spectroscopy, atomic force microscopy, X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry and dynamic mechanical analysis and mechanical properties testing were used to determine the differences in the structure and properties of the initial copolymers and targeted products. The effect of the conditions of destructive processes on the structure, morphology and mechanical properties of the obtained porous polyimide films was determined. From a practical point of view, the final porous films are promising as membranes for filtering aggressive amide solvents at high temperatures.