Synthesis of Silver Nanoparticle/Multi-Walled Carbon Nanotube Composites and Their Application in Electronic Pastes.

Silver nanoparticle-coated multi-walled carbon nanotube (Ag/MWNT) composites were prepared using a chemical plating method that effectively controls the overgrowth of silver nanoparticles, ensuring uniform particle size. Functionalization of the carbon nanotube surface with numerous functional groups facilitates the binding of silver ions to multi-walled carbon nanotubes (MWNTs). This process results in Ag/MWNT composites with a uniform distribution of silver nanoparticles, prepared through reduction via the silver mirror reaction. The impact of dispersants and reducing agents on the silver coating of carbon nanotubes was studied. The results revealed the formation of negatively charged functional groups (-COOH, -OH, -C=O, and -NH2) on the nanotube surface. These groups acted as nucleation sites for the formation of silver nanoparticles. These groups acted as nucleation sites for the formation of silver nanoparticles. Simultaneously, the Ag/MWNT composites demonstrated effective dispersion within the matrix, improving the electrical conductivity of the electronic paste by 32.1% and 33.1%. This improvement was attributed to the forming of a conductive pathway within the silver-modified composite. Ag/MWNT composites within the paste system improved interfacial contact between fillers and the matrix, enhancing their potential applications in thermal interface materials.