ArticleBeijing da xue xue bao. Yi xue ban = Journal of Peking University. Health sciences2025
[Cyclic fatigue resistance of nickel-titanium files made by Gold heat treatment in simulated S-shaped root canals at different temperatures].
Article in Beijing da xue xue bao. Yi xue ban = Journal of Peking University. Health sciences, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
objectiveTo compare the cyclic fatigue resistance of nickel-titanium files made by 3 new heat treatment in simulated S-shaped root canals at different temperatures.
methodsGold heat-treated nickel-titanium files TruNatomy (25 mm, tip size 26#/0.04) and ProTaper Gold (25 mm, tip size 25#/0.08) were selected as the experimental group, M wire technique nickel-titanium file ProTaper Next (25 mm, tip size 25#/0.06) was selected as the control group. It was speculated that the Gold technique used in TruNatomy nickel-titanium file was R phase separation technique, which included a complete intermediate R-phase, increasing its flexibility. ProTaper Gold was a CM wire nickel-titanium file and the increased phase transformation temperature by heat treatment introduced martensite at room temperature, while it underwent gold heat treatment on the surface, generating an intermediate R phase during phase transformation, providing hyperelastic. ProTaper Next used M wire technique, M wire included austenite at room temperature, where heat mechanical processing introduced hardened martensite, which was incapable of participating phase transformation. Because of the lower elastic modulus of hardened martensite than austenite, the flexibility of the file was increased. Twenty instruments of each nickel-titanium file were submitted to the cyclic fatigue test by using a simulated canal with double curvatures at room tem-perature (24 ℃) and 65 ℃, 10 instruments of each nickel-titanium file were selected at each temperature (
resultsIn double-curved canals, all the failure of the files due to cyclic fatigue was first seen in the apical curvature before the coronal curvature. At room temperature, in the apical curvature, NCF of TruNatomy was 344.4±96.6, ProTaper Gold was 175.0±56.1, ProTaper Next was 133.3±39.7, NCF of Tru Natomy was the highest (
conclusionGold heat-treated nickel-titanium file had better cyclic fatigue resistance than M wire nickel-titanium file in S-shaped root canals.