ArticleBiomimetics (Basel, Switzerland)2025
Influence of the Sodium Titanate Crystal Size of Biomimetic Dental Implants on Osteoblastic Behavior: An In Vitro Study.
Article in Biomimetics (Basel, Switzerland), 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Controlling Sodium Titanate Crystal Size to Improve Wettability and Early Osseointegration of Titanium Implants: Insights from an Animal Model.Journal of functional biomaterials · 2025Article
- Piezoelectric-immunomodulatory electrospun membrane for enhanced repair of refractory wounds.Journal of nanobiotechnology · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Treating the surfaces of dental implants in an alkaline medium allows us to obtain microstructures of sodium titanate crystals that favor the appearance of apatite in the physiological environment, producing osteoconductive surfaces. In this research, 385 discs made of titanium used in dental implants underwent different NaOH treatments with a 6M concentration at 600 °C and cooling rates of 20, 50, 75, and 115 °C/h. Using high-resolution electron microscopy, the microstructures were observed, and the different crystal sizes were determined and compared with control samples (those without biomimetic treatment). Roughness, wettability, surface energy and the sodium content of the surface were determined. The different surfaces were cultured with human osteoblastic cells; cell adhesion was determined at 3 and 14 days, and the degree of mineralization was determined at 14 days via alkaline phosphatase levels. Variations in the microstructure and size of sodium titanate crystals in NaOH solutions rich (1 g/L) or low in calcium (approximately 100 ppm) were determined. The results show that as the cooling rate increases, the size of the crystals decreases (from 0.4 μm to 0.8 μm) except for the case of 115 °C/h, when the rate is too fast for crystalline nucleation to occur on the surface of the titanium. The thermochemical treatment does not influence the roughness or the cooling rate since a Sa of 0.21 μm is maintained. However, the presence of titanate causes a decrease in the contact angle from 70° to 42° and, in turn, causes an increase in the total surface energy from 35 to 49.5 mJ/m