ArticleDental materials : official publication of the Academy of Dental Materials2025
Experimental bilayer zirconia systems after aging: Mechanical, optical, and microstructural characterization.
Article in Dental materials : official publication of the Academy of Dental Materials, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Fatigue Performance and Failure Loads of Composition-Gradient Multilayer Zirconia: Partial-Coverage Restorations Versus Single Crowns at Different Thicknesses.Journal of esthetic and restorative dentistry : official publication of the American Academy of Esthetic Dentistry ... [et al.] · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
16 authors.
Funding
Abstract
objectivesTo characterize two experimental zirconia bilayer materials compared to their monolithic controls, before and after hydrothermal aging.
methodsCommercial zirconia powders were utilized to fabricate two bilayer materials: 3Y-TZP+ 5Y-PSZ (3Y+5Y/BI) and 4Y-PSZ+ 5Y-PSZ (4Y+5Y/BI), alongside control groups 3Y-TZP (3Y/C), 4Y-PSZ (4Y/C), and 5Y-PSZ (5Y/C). Compacted specimens were sintered (1550 °C- 2 h, 3 °C/min), and half of them underwent hydrothermal aging (134 °C-20h, 2.2 bar). Characterizations were performed through scanning-electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy, reflectance tests and biaxial flexural strength test (ISO:6872). Weibull statistics were applied to determine the characteristic strength and Weibull modulus. Grain size and optical properties were analyzed using two-way ANOVA followed by the Tukey test.
resultsDegradation regions and monoclinic phase were observed at aged 3Y-TZP and 4Y-PSZ surfaces. Significant differences were observed in the evaluation of optical properties between the bilayer and control groups. The bilayer materials presented intermediate characteristic strength values compared to their controls and aging significantly increased the strength of some groups. SIGNIFICANCE: Experimental bilayer materials presented lower mechanical properties than monolithic controls, 3Y/C and 4Y/C. Hydrothermal aging increased the characteristic strength of bilayered and monolithic controls, except for 5Y-PSZ. Both experimental bilayer systems, as well as monolithic controls, met the ISO 6872:2015 requirements for single-unit crowns (100 MPa), 3-unit fixed dental prostheses (FDPs) up to premolars (300 MPa), and 3-unit FDPs involving molars (500 MPa). However, for FDPs with four or more units, only monolithic 3Y-TZP and 4Y-PSZ, and bilayered 3Y+5Y met the required minimum flexural strength (≥800 MPa).