Synergistic design of CuO/CoFe₂O₄/MWCNTs ternary nanocomposite for enhanced photocatalytic degradation of tetracycline under visible light.

This study involves a novel CuO/CoFe₂O₄/MWCNTs (CCT) nanocomposite, developed by integrating cobalt ferrite (CoFe₂O₄) and copper oxide (CuO) nanoparticles onto multi-walled carbon nanotubes (MWCNTs), for the degradation of tetracycline (TC) under visible light. The photocatalyst was extensively characterized using XRD, HR-SEM, EDX, HR-TEM, UV-Vis, BET, and PL analysis. The synthesized CoFe₂O₄ and CuO nanoparticles exhibited crystallite sizes of 46.8 nm and 37.5 nm, respectively, while the CCT nanocomposite had a crystallite size of 53 nm. Microscopy confirmed a particle size of 49.2 nm for the nanocomposite, with MWCNTs measuring 15.65 nm in diameter. The band gap energy of the CCT nanocomposite was 1.6 eV, which contributed to its enhanced photocatalytic activity, as evidenced by the lower emission intensity in PL analysis. BET analysis revealed a pore volume of 0.37 cc/g and a surface area of 82.3 m²/g. Photocatalytic performance was tested across various conditions, with adjustments to nanocomposite dosages (0.1-0.5 g/L), TC concentrations (5-25 mg/L), and pH levels (2-10). Under optimized conditions (0.3 g/L CCT, 5 mg/L TC, pH 10, 120 min of visible light exposure), the CCT achieved 98.1% degradation of TC. The optimized parameters were subsequently used to assess TC degradation with individual photocatalysts: CoFe₂O₄, CuO, CT, and CCT. The enhanced photocatalytic efficiency observed can be largely attributed to the improved charge transfer dynamics and effective electron-hole separation facilitated by MWCNT doping. The reaction followed a pseudo-first-order kinetic model, with hydroxyl radicals (OH