Gradient Titanium Alloy with Bioactive Hydroxyapatite Porous Structures for Potential Biomedical Applications.

Hard bone disease is a clinical problem affecting more than 20 million people annually worldwide, with significant health, social, and economic consequences. For successful integration of any implant, the key aspects are bone regeneration, osseointegration at the bone-implant interface, and the mitigation of inflammation. The purpose of this research work is to demonstrate an innovative material system and method of biomaterial preparation for regenerative medicine. A number of studies were carried out for both hydroxyapatite powder and composites. Wet-precipitated synthesized hydroxyapatite was compared to commercial products through accurate physicochemical studies that confirmed the high purity of the obtained calcium phosphate without any impurities. Ti/HAp composites before and after sintering were compared by XRF, XRD, SEM, EDS, PSA, and roughness measurements, and the Vickers microhardness was analyzed. The fabrication of the biomaterial was based on a bottom-up approach, which involved fabricating HAp particles with specific morphologies using powder metallurgy (PM) to sinter Ti composites. The resulting gradient structures consisting of two compositions (5%HAp%5CMC and 10%HAp10%CMC) mimic the structure of bone tissue. The created pores of 10-100 µm in size will allow bone cells to penetrate the implant and regenerate bone. In turn, the introduction of hydroxyapatite into the material reduces the microhardness of the composite and introduces properties such as bioactivity. The developed composite material contains a combination of Ti alloy and hydroxyapatite (HAp), creating an excellent biomaterial that promotes bone growth and eliminates the problem of implant loosening by integrating it into the bone. This material requires further research, especially biological research. However, it shows promising potential for further experiments.