ArticleJournal of the mechanical behavior of biomedical materials2025
Sequential irradiation does not improve fatigue crack propagation resistance of human cortical bone at 15 kGy.
Article in Journal of the mechanical behavior of biomedical materials, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
Abstract
Sequential irradiation has been advocated for mitigating the reduction in fatigue properties of tendon compared to a single dose. However, to our knowledge, its capability of mitigating fatigue losses in bone is unknown. Recently, we reported that sequential irradiation did not mitigate losses in high-cycle S-N fatigue life of cortical bone at 15 kGy; however, it is unclear if sequential irradiation provides a benefit to fatigue crack propagation resistance. Our previous study also showed that radiation-induced collagen chain fragmentation and crosslinking increased from 0 to 15 kGy, suggesting that both likely contribute to the reduction in high-cycle S-N fatigue life within this dose range. Our objectives were: 1) to evaluate the fatigue crack propagation resistance of cortical bone and the effect of radiation on fracture plane damage zone thickness (DZT) at the crack tip in the dose range of 0-15 kGy, and 2) to evaluate whether sequential irradiation at 15 kGy mitigates the loss of fatigue crack propagation resistance of cortical bone compared to a single irradiation dose. Compact tension specimens from four male donor femoral pairs (ages 21-61 years old) were divided into 5 treatment groups (0 kGy, 5 kGy, 10 kGy, 15 kGy, and a 15 kGy sequential irradiation dose of 5 kGy sequentially irradiated with 10 kGy) and subjected to fatigue crack propagation testing (n = 3-4 specimens per group) where fatigue crack growth rate da/dN and cyclic stress intensity factor ΔK were determined. Following testing, specimens were bulk stained in basic fuchsin, embedded in poly(methylmethacrylate), sectioned, and mounted on acrylic slides to evaluate fracture plane DZT at known crack lengths. Sections were then imaged with a fluorescence microscope, and fracture plane DZT was measured using ImageJ (n = 3-4 specimens per group) and analyzed as a function of ΔK. We observed a decrease in fatigue crack propagation resistance at 15 kGy compared to doses of 10 kGy or lower (p ≤ 0.013). Fracture plane DZT decreased overall with increasing radiation dose from 0 to 15 kGy. Sequential irradiation offered no improvement in fatigue crack propagation resistance (p = 0.98). Radiation-induced collagen chain fragmentation and crosslinking in this dose range likely contribute to a decrease in energy dissipation capability with increasing radiation dose. Other alternative radiation sterilization methods besides sequential irradiation may be warranted to mitigate radiation-induced tissue damage and extend the functional lifetime of structural cortical bone allografts.