Highly Robust, Pressureless Silver Sinter-Bonding Technology Using PMMA Combustion for Power Semiconductor Applications.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
This study presents the development of a highly robust, pressureless, and void-free silver sinter-bonding technology for power semiconductor packaging. A bimodal silver paste containing silver nanoparticles and sub-micron particles was used, with polymethyl methacrylate (PMMA) as an additive to provide additional thermal energy during sintering. This enabled rapid sintering and the formation of a dense, void-free bonding joint. The effects of sintering temperature and PMMA content on shear strength and microstructure were systematically investigated. The results showed that the shear strength increased with rising sintering temperatures, achieving a maximum of 41 MPa at 300 °C, with minimal void formation due to enhanced particle necking facilitated by PMMA combustion. However, at 350 °C, the shear strength decreased to 35 MPa due to cracks and voids at the copper substrate-copper oxide interface caused by thermal expansion mismatch. The optimal PMMA content was found to be 5 wt.%, balancing sufficient thermal energy and void reduction. This pressureless sintering technology demonstrates significant potential for high-reliability applications in power semiconductor modules operating under high-temperature and high-stress conditions.