Grain Microstructure in Friction-Stir-Welded Dissimilar Al/Mg Joints of Thin Sheets with/without Ultrasonic Vibration.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Advances in Materials Joining and Additive Manufacturing.Materials (Basel, Switzerland) · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Electron backscattered diffraction (EBSD) characterization was conducted on the typical regions in friction-stir-welded dissimilar Al/Mg joints of 2 mm thick sheets with/without ultrasonic assistance. The effects of ultrasonic vibration (UV) on the grain size, recrystallization mechanisms, and degree of recrystallization on both sides of the Al-Mg bonding interface and the intermetallic compounds (IMCs) were investigated. It was found that on the Mg side of the weld nugget zone (WNZ), the primary dynamic recrystallization (DRX) mechanisms were discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX), with geometric dynamic recrystallization (GDRX) playing a secondary role. On the Al side of the WNZ, CDRX was identified as the primary mechanism, with GDRX as a secondary contributor. While UV did not significantly alter the DRX mechanisms in either alloy within the WNZ, it promoted the aggregation and rearrangement of dislocations. This led to an increase in high-angle grain boundaries (HAGBs) and an enhanced degree of recrystallization in the welds. The average grain size in both the Al and Mg alloys of the WNZ followed a pattern of initially increasing and then decreasing along the thickness direction, reaching a maximum in the upper-middle part and a minimum at the bottom. The influence of UV on the average grain size in the WNZ was minimal, with only slight grain refinement observed, and the minimum refinement degree was only 0.9%. The Schmid factor (SF) on the WNZ and thermo-mechanically affected zone (TMAZ) boundary regions of the advancing side (AS) indicates that the application of UV increased the likelihood of basal slip and extension twinning in the crystal structure. In addition, UV reduced the thickness of IMCs and improved the strength of the Al-Mg bonding interface. These results suggest a higher probability of fracture along the TMAZ and WNZ boundary on the AS when UV was applied.