Enhancing Fire Resistance of Geopolymers Modified with Thermal Insulation Additives.

This study aims to improve the fire resistance of geopolymers by adding thermal insulation materials. These additives help the material perform better at high temperatures. Previous research focused on using fly ash, metakaolin, and zeolite in geopolymer composites. This study looks at how porous additives affect compressive strength and whether non-destructive testing can measure damage after heat exposure. Four temperature tests were set: 400 °C for 60 min, 400 °C for 120 min, 800 °C for 60 min, and a maximum of 658 °C for 120 min. The results showed that the compressive strength and ultrasonic pulse velocity (UPV) dropped as the temperature increased, with a sharp decrease at 800 °C. Unmodified samples broke apart at high temperatures, while modified samples lost 40% to 70% of their strength. The study confirmed that a dense, amorphous matrix improves heat resistance, even with porous additives like fly ash. A link between UPV and compressive strength was found, suggesting non-destructive testing could be useful for checking structural integrity after a fire.