Effect of glass infiltration and modified cooling rates on color characteristics alteration of monochrome and multilayer high yttrium oxide containing zirconia.
Article in Journal of clinical and experimental dentistry, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Background: Sintering technique impacted color of zirconia. This study examined the effect of glass infiltration and altering cooling rate on color alteration of monochrome (Mo) and multilayer (Mu) 5 mol% yttria-partially stabilized zirconia (5Y-PSZ). Material and Methods: 180 specimens (width, length, thickness = 10, 20, 2 mm) were prepared from Mo and Mu (comprising cervical (C) and incisal (I) zone) 5Y-PSZ shade VITA-A2. Unintentionally categorized samples (n=15/group) were sintered with traditional (T) versus glass infiltrated (G) technique and cooled down with slow (S: 5°C/min), normal (N: 35°C/min), and fast (F: 70°C/min). CIE-L*a*b* color characteristics were determined for translucency parameter (TP), contrast ratio (CR), opalescence parameter (OP), and color difference (∆Ediff). Microstructures were investigated with SEM and XRD. ANOVA and Tamhane's comparisons were determined for significant differences ( Results: TP and OP were significantly higher for Mo than MuC and MuI, but no significant difference in CR among them. Comparable ΔEdiff between Mo and MuC were indicated, but both were significantly lesser than MuL. Glass infiltration and raising cooling rate significantly decreased TP and OP, whereas increased CR and ΔEdiff, which amplified color alteration. Conclusions: Glass infiltration sintering and modified cooling rate significantly altered color parameters of 5Y-PSZ. Monochrome demonstrated higher translucency and opalescence than multilayer, possibly due to colorant additives. Glass infiltration decreased translucency and opalescence due to different refractive indices. Increased cooling rate resulted in decreasing translucency and opalescence due to smaller grain size and t→m transformation. Nevertheless, altered sintering and cooling rates still rendered an acceptable color alteration.
Identifiers
What OpenQuestion holds
Registered trials
Read under generation 80e0d062 · epoch 390. Bibliography from PubMed, PubMed Central and OpenAlex; grants from NIH RePORTER; trial links from ClinicalTrials.gov; estimates, votes and beliefs from the OpenQuestion graph.