Enhancing antifungal and antibacterial properties of denture resins with nystatin-coated silver nanoparticles.

Long-term oral health issues caused by fungi and bacteria are a primary concern for individuals who wear dentures. Denture stomatitis, primarily caused by Candida albicans (C. albicans), is a prevalent condition among denture users. Metal nanoparticles exhibit improved antimicrobial effectiveness and fewer adverse effects. This study aimed to evaluate the antifungal and antibacterial effects of nystatin-coated silver nanoparticles (Nys-coated AgNPs) embedded in acrylic resin as a more biocompatible material for denture resins. AgNPs and Nys-coated AgNPs were synthesized and characterized using UV-Vis, SEM, EDX, and DLS. Specimens of polymethyl methacrylate (PMMA) with three different concentrations of Nys, AgNPs, and Nys-coated AgNPs (0.1%, 1%, 10% w/w) were prepared. The water absorption properties of the disks and drug release were investigated for 14 days and 120 h, respectively. The hydrophilic and hydrophobic properties of the samples and their contact angles were evaluated using the sessile drop technique. The antifungal and antimicrobial activity of the prepared discs was studied against C. albicans and Streptococcus mutans, respectively. Adding Nys-coated AgNPs decreased the contact angle of discs from 67° to 49°. Furthermore, the water absorption rates of the different discs were not significantly different from those of the control groups. Results showed that Nys-coated AgNPs (10% w/w) in PMMA effectively inhibited C. albicans growth better than Nys composites (10% w/w). Additionally, Nys-coated AgNPs composites, as well as AgNPs-containing composites, showed considerable antibacterial activity against S. mutans. Nys-coated AgNPs (10% w/w) had no toxic effect on NIH3T3 cells. In conclusion, Nys-coated AgNPs could be considered a good candidate for incorporation into denture resins to address chronic oral diseases.