Influence of Zinc Chloride Exposure on Microstructure and Mechanical Behavior of Age-Hardened AZ91 Magnesium Alloy.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
The AZ91 magnesium alloy was subjected to a complex treatment involving age hardening (supersaturation and artificial aging) and simultaneous surface layer modification. The specimens were supersaturated in contact with a mixture containing varying concentrations of zinc chloride, followed by cooling either in air or water. After supersaturation, the specimens were subjected to artificial aging and then air-cooled. This process resulted in the formation of a surface layer made of zinc-rich phases. The thickness and microstructure of the surface layer were influenced by the process parameters, namely, the zinc chloride content in the mixture and the cooling rate during supersaturation. The treated specimens exhibited favorable tensile strength and greater elongation compared to the as-cast AZ91 alloy, with values comparable to those of the alloy subjected to standard T6 tempering. No cracking of the layer was observed under moderate deformation, though greater deformation resulted in the formation of cracks, primarily in the areas containing the Mg