[Physical, chemical, and biological property of silk reinforced polycaprolactone composites for bone tissue engineering].

Objective: To develop a biodegradable implantable bone material with compatible mechanics with the bone tissue, providing a new biomaterial for clinical bone repair and regeneration. Methods: Silk reinforced polycaprolactone composites (SPC) containing 20%, 40%, and 60% silk were prepared by layer-by-layer assembly and hot-pressing technology. Macroscopic morphology was observed and microstructure were observed by scanning electron microscopy, compressive mechanical properties were detected by compression test, surface wettability was detected by surface contact angle test, degradation of materials was observed after soaking in PBS for 180 days, and proliferation of MC3T3-E1 cells was detected by cell counting kit 8 assay. Six Sprague Dawley rats were subcutaneously implanted with polycaprolactone (PCL) and 20%-SPC, respectively. Masson staining was used to analyze the Results: The pore defects of the three SPC sections were relatively few. In the range of 20% to 60%, as the silk content increased and the PCL content decreased, the interlayer spacing of silk fabric decreased, and the fibers almost covered the entire cross-section. The compressive modulus and compressive strength of SPC showed an increasing trend, and the compressive modulus of 60%-SPC was slightly lower than that of 40%-SPC. There were significant differences in compressive modulus and compressive strength between the materials ( Conclusion: SPC has the mechanical and hydrophilic properties that are compatible with bone tissue. It maintains its mechanical strength for a long time in a simulated body fluid environment