Study of cracks in the last-stage rotor blade of a steam turbine and the corrosion fatigue properties of its materials.
Article in Heliyon, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
In this study, to clarify the failure mechanism of the last-stage rotor blade in the low-pressure cylinder of a steam turbine, the peculiarities of crack initiation and propagation on the inlet side of the last-stage rotor blade at a distance of 125-165 mm were analyzed, along with the corrosion fatigue properties of its materials. The results showed that crack initiation occurred at the tip of the pit due to a combination of factors: stress concentration at the tip of the pit, corrosion of the Cr-poor area near the prior austenite grain boundary, centrifugal tensile stress, and steam bending stress. The crack propagation could be divided into the initial intergranular and late transgranular propagation stages. The main reason for the initial intergranular propagation was stress corrosion, and the main reason for the later transgranular propagation was corrosion fatigue. High-frequency induction quenching technology can improve the microhardness of the blade's surface material and enhance the blade's resistance to water erosion, but it may also reduce the corrosion fatigue resistance of the blade material. The rotary bending corrosion fatigue test can effectively simulate the crack propagation process of the blade. These results are of great significance for the safe operation of the last-stage rotor blade in the low-pressure cylinder of a steam turbine.