The Surface Deterioration of Prefabricated Zirconia Crowns on Exposure to Acidulated Phosphate Fluoride Gel: An In Vitro Study.
Article in Cureus, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
10 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Introduction Zirconia is a widely used restorative material in dentistry due to its superior aesthetic and mechanical properties. The oral cavity is a complex ecosystem with various components, which affect the teeth, as well as artificial restorative materials. Various personal and professional interventions carried out can severely affect the properties of restorative materials, thus altering the longevity of the prosthesis; 1.23% acidulated phosphate fluoride (APF) gel is one such professionally applied topical fluoride agent used to prevent caries. The interaction of this APF gel with highly aesthetic restorative material such as zirconia crowns is unknown. Objective The objective of this study is the evaluation of the surface deterioration of prefabricated zirconia crowns on exposure to deionised water and 1.23% acidulated phosphate fluoride (APF) gel with field emission scanning electron microscope (FE-SEM) and mass loss analysis. Material and method Sixty prefabricated paediatric zirconia crowns were taken, 10 samples were immersed in deionised water, 40 samples were immersed in 1.23% APF gel and 10 samples were used as control. Surface morphology and mass loss analysis were carried out at time intervals of four minutes, 24 hours, 48 hours and 72 hours using FE-SEM and digital weighing machine. Results No visual change was observed in the samples immersed in deionised water at the time interval of 72 hours. There was a marked visual change in samples immersed in 1.23% APF gel at the time interval of four minutes to 72 hours; this change involved a loss of gloss to the appearance of chalkiness. FE-SEM analysis for the control group and samples immersed in deionised water showed a smooth, continuous, undisrupted top layer, while samples immersed in 1.23% APF gel showed changes ranging from surface etching, to pinhole porosities, to crack formation and disruption of the surface depending upon the exposure time. Conclusions On the immersion of zirconia crowns in an aqueous acidic medium of 1.23% APF gel, the crowns showed flaws, imperfections and uneven superficial layers. It has been observed that surface grains are disrupted and micropores have been formed. This degraded superficial surface when undergoes cyclic mechanical loading can accelerate the ageing phenomenon of zirconia. Mechanical forces along with a dynamic electrochemical environment can degrade the material properties of zirconia.