Influence of build direction, post-polymerization time, and aging on the fracture resistance and marginal and internal discrepancies of three-dimensional printed provisional crowns.
Article in Odontology, 2025. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Three-Dimensional Printing Resin-Based Dental Provisional Crowns and Bridges: Recent Progress in Properties, Applications, and Perspectives.Materials (Basel, Switzerland) · 2025Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
To evaluate the effect of build direction, post-polymerization time, and aging on the fracture resistance, failure mode, margin quality and Marginal (MD) and Internal Discrepancies (ID), and degree of conversion of tridimensional (3D) printed provisional crowns using the liquid crystal display technique (LCD). A left mandibular first molar was prepared and scanned. After, a full crown was designed (ExoCad) and exported to the LCD-printer software. One hundred and eighty crowns were printed at two build directions (30°, 90°) and post-polymerized for different periods (15, 30, 45 min). Half of the samples were aged (ST) in distilled water (37 °C/90 days). The marginal quality of the crowns was evaluated by the Schriwer method under a stereomicroscope (40x). The replica technique was used to measure the MD and ID and measured under a stereomicroscope (10x), through 20 reference points defined in 5 regions: Occlusal (O), Cusp (CP), Axial (AX), Chamfer (CH), and Finish Line (F). After, the crowns were cemented onto the respective dies using temporary cement and submitted to compression test (ISO150, 1 mm/min, 100 kgf).The failure mode was classified by Burke's fracture mode. The degree of conversion was evaluated through Fourier Transform Infrared Spectroscopy. The data (μm) of MD and ID and fracture resistance (N) were subjected to ANOVA (3 factors) and Tukey's test (5%); Weibull analysis was also performed for fracture resistance data (N). For MD, ID and fracture resistance ANOVA revealed that all factors (P < .001) were significant. For aged groups, the crowns printed at 30° showed lower MD (Tukey). The O_90_30 min (172.13