Exploring the Relationship between Mechanical Properties and Electrical Impedance in Cement-Based Composites Incorporating Gold Nanoparticles.

Structural health monitoring applications have gained significant attention in recent research, particularly in the study of the mechanical-electrical properties of materials such as cement-based composites. While most researchers have focused on the piezoresistive properties of cement-based composites under compressive stress, exploring the electrical impedance of such materials can provide valuable insights into the relationship between their mechanical and electrical characteristics. In this study, we investigated the connection between the mechanical properties and electrical impedance of cement-based composites modified with Au nanoparticles. Cylindrical samples with dimensions of 3 cm in diameter and 6 cm in length were prepared with a ratio of w/c = 0.47. The Au nanoparticles (Au NPs) were synthesized using pulsed laser ablation in liquids, and their size distribution was analyzed through dynamical light scattering. Mechanical properties were evaluated by analyzing the Young modulus derived from strain-stress curves obtained at various force rates. Electrical properties were measured by means of electrical impedance spectroscopy. The experimental results revealed a notable reduction of 91% in the mechanical properties of Au NPs-cement compounds, while their electrical properties demonstrated a significant improvement of 65%. Interestingly, the decrease in mechanical properties resulting from the inclusion of gold nanoparticles in cementitious materials was found to be comparable to that resulting from variations in the water/cement ratios or the hydration reaction.