ArticleMaterials (Basel, Switzerland)2024
Hot Crack Formation Mechanism and Inhibition of a Novel Cobalt-Based Alloy Coating during Laser Cladding.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Research Progress in and Defect Improvement Measures for Laser Cladding.Materials (Basel, Switzerland) · 2025Review
- Advanced Multi-Objective Optimization for Laser Cladding of H13 Die Steel with CFOA.Materials (Basel, Switzerland) · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
9 authors.
Funding
Abstract
Laser cladding provides advanced surface treatment capabilities for enhancing the properties of components. However, its effectiveness is often challenged by the formation of hot cracks during the cladding process. This study focuses on the formation mechanism and inhibition of hot cracks in a novel cobalt-based alloy (K688) coating applied to 304LN stainless steel via laser cladding. The results indicate that hot crack formation is influenced by liquid film stability, the stress concentration, and precipitation phases. Most hot cracks were found at 25°-45° high-angle grain boundaries (HAGBs) due to the high energy of these grain boundaries, which stabilize the liquid film. A flat-top beam, compared to a Gaussian beam, creates a melt pool with a lower temperature gradient and more mitigatory fluid flow, reducing thermal stresses within the coating and the fraction of crack-sensitive, high-angle grain boundaries (S-HAGBs). Finally, crack formation was significantly inhibited by utilizing a flat-top laser beam to optimize the process parameters. These findings provide a technical foundation for achieving high-quality laser cladding of dissimilar materials, offering insights into optimizing process parameters to prevent hot crack formation.