Quasi-static and dynamic mechanical properties of a linoleic acid-modified, low-modulus bone cement for spinal applications.
Article in Open research Europe, 2023. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
4 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Background: Polymethylmethacrylate (PMMA) bone cement is extensively used in spinal procedures such as vertebroplasty and kyphoplasty, while its use in percutaneous cement discoplasty (PCD) is not yet widely spread. A main issue for both application sites, vertebra and disc, is the mismatch in stiffness between cement and bone, potentially resulting in adjacent vertebral fractures and adjacent segment disease. Tailoring the cement modulus using additives is hence an interesting strategy. However, there is a lack of data on the tensile and tension-compression fatigue properties of these cements, relevant to the newly researched indication of PCD. Method: A commercial PMMA cement (VS) was modified with 12%vol of linoleic acid (VSLA) and tested for quasi-static tensile properties. Additionally, tension-compression fatigue testing with amplitudes ranging from +/-5MPa to +/-7MPa and +/-9MPa was performed, and a Weibull three-parameter curve fit was used to calculate the fatigue parameters. Results: Quasi-static testing revealed a significant reduction in VSLA's Young's Modulus (E=581.1±126.4MPa) compared to the original cement (E=1478.1±202.9MPa). Similarly, the ultimate tensile stress decreased from 36.6±1.5MPa to 11.6±0.8MPa. Thus, VSLA offers improved compatibility with trabecular bone properties. Fatigue testing of VSLA revealed that as the stress amplitude increased the Weibull mean number decreased from 3591 to 272 and 91 cycles, respectively. In contrast, the base VS cement reached run-out at the highest stress amplitude. However, the lowest stress amplitude used exceeds the pressures recorded in the disc Conclusions: While the relevance of fully reversed tension-compression fatigue testing can be debated for predicting cement performance in certain spinal applications, the results of this study can serve as a benchmark for comparison of low-modulus cements for the spine. Further investigations are necessary to assess the clinical feasibility and effectiveness of these cements.