ArticleMaterials (Basel, Switzerland)2024
Influence of Ultraviolet Light and Alternating Wet-Dry Environments on the Corrosion Behavior of Weathering Steels.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Carbon starvation enhances microbiologically influenced corrosion in marine offshore infrastructures.Frontiers in microbiology · 2026Article
- Behavior of Weathering Steel in Artificial Harsh Environment.Materials (Basel, Switzerland) · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
Abstract
The corrosion behaviors of two bridge steels (Q345q and Q500q) under simulated ultraviolet irradiation and a wet-dry alternating (UVWD) environment were studied. Weight loss measurement, stereomicroscope observation, SEM, XRD, and electrochemical impedance spectroscopy (EIS) were performed to investigate the influence of the coupled environment. The results revealed that the corrosion rates of Q345q and Q500q were significantly accelerated by the synergistic effect of UV light exposure and alternating wet-dry conditions. Numerous voids and cracks could be observed throughout the thickened rust layers, enabling the corrosive substances to easily penetrate through the rust layer. Q500q exhibited better corrosion resistance than Q345q due to the addition of Mo, Cr, and Ni as corrosion-resistant elements, which tended to transform the rust layer into α-FeOOH rather than γ-FeOOH during later stages of corrosion.