Fatigue Strength Improvement of Laser-Directed Energy Deposition 316L Stainless Steel with In Situ Ultrasonic Rolling by Preliminary Investigation.
Article in Materials (Basel, Switzerland), 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Not yet cited in PubMed.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
0 citing papers in PubMed.
No citing paper in PubMed yet.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
In this study, to improve the fatigue strength of the LDED (laser-directed energy deposition) 316L stainless steel, an in situ ultrasonic rolling technology is developed to assist the laser-directed energy deposition process (LDED-UR). The microstructural characteristics and fatigue behavior are comprehensively discussed. The results show that the average size of pores of the LDED-UR alloy is about 10.2 μm, which is much smaller than that of the LDED alloy (34.1 μm). Meanwhile, the density of the LDED alloy is also enhanced from 98.26% to 99.27% via the in situ ultrasonic rolling. With the application of the in situ ultrasonic rolling, the grains are transformed into fully equiaxed grains, and their average grain size is greatly reduced from 84.56 μm to 26.93 μm. The fatigue limit of the LDED-UR alloy is increased by 29% from 210 MPa (LDED alloy) to 270 MPa, which can be ascribed to the decreased porosity and the fine grains. In particular, the crack initiation site of the LDED alloy is located at the surfaces, while it is nucleated from the sub-surface for the LDED-UR alloy. This is mainly attributed to the compression residual stress induced by the in situ ultrasonic rolling. This research offers a valuable understanding of the failure mechanisms in additively manufactured metals, guiding the development of effective strategies to improve their fatigue threshold under severe operating conditions.