A protocol for a comparative evaluation of the fracture resistance of endodontically treated teeth reinforced with Cention N, resin-modified glass ionomer cement (RMGIC) and short fiber reinforced flowable composite as an intraorifice barrier.

Background: Endodontic treatment is the most common method for resolving pulpal and periapical pathology. However, various studies have reported that almost 11%-13% of all teeth that undergo extraction after endodontic treatment show the presence of cracks, craze lines, and vertical root fractures. Teeth with inadequate post endodontic restoration are more prone to fracture and coronal leakage, resulting in the diffusion of oral fluids, bacteria, bacterial products, and possibly root canal treatment failure. Furthermore, studies have advocated the use of endodontically treated teeth with restorative materials that have a similar or higher elastic modulus than the tooth for providing stiffness against forces that cause root fracture. Intraorifice barriers made of restorative materials that can bond to radicular dentin could thus be used to reinforce the radicular dentin while also preventing coronal microleakage. Although the sealing ability of intraorifice barriers has been widely compared in the literature, there have been few studies on the strengthening effect of the materials used in the study as intraorifice barriers when placed into the root canal. As a result, the current Methods: This