Variations in the Thermomechanical and Structural Properties during the Cooling of Shape-Memory R-PETG.
Article in Polymers, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
7 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
One of the useful features of 3D-printed specimens of recycled polyethylene terephthalate glycol (R-PETG) is the ability to repetitively develop free recovery as well as the work-generating, shape-memory effect. This behavior is enabled by the R-PETG's capacity to stiffen during cooling, thus allowing for a new temporary shape to be induced. Aiming to devise an explanation for the polymer's stiffening, in this study, the variation in some of the R-PETG's parameters during cooling are emphasized and discussed. The evolution of an R-PETG filament's shape was monitored during room-temperature-bending heating-cooling cycles. Straight-shape recovery and the complete loss of stiffness were observed at the start and the end of heating, respectively, followed by the forced straightening of the filament, performed by the operator, around 40 °C, during cooling. The tests performed by dynamic mechanical analysis disclosed the rise of the storage modulus (E') after 100 °C heating followed by either liquid-nitrogen- or air-cooling to room temperature, in such a way that E' was always larger after cooling than initially. Static tests emphasized a peculiar stress variation during a heating-cooling cycle applied in air, within the heating chamber of the tensile testing machine. Tensile-failure tests were performed at -10 °C at a rate of 100 mm/min, with specimens printed at various deposition directions between 10 and 40° to the transversal direction. The specimens printed at 40°, which had the largest ultimate strains, were broken with tensile rates between 100 and 500 mm/min. Deformation rate increase favored the shift from crazing to delamination failure modes. The correlation between the structural changes, the sharp E' increase on heating, and the stiffening induced by cooling represents a novel approach that enables the use of 3D-printed R-PETG for the fabrication of the active parts of low-priced lightweight resettable actuators.