Effect of Diffusion on the Ultimate Axial Load of Complex-Shaped Al-SiC Samples: A Molecular Dynamics Study.

Metal matrix composites (MMCs) combine metal with ceramic reinforcement, offering high strength, stiffness, corrosion resistance, and low weight for diverse applications. Al-SiC, a common MMC, consists of an aluminum matrix reinforced with silicon carbide, making it ideal for the aerospace and automotive industries. In this work, molecular dynamics simulations are performed to investigate the mechanical properties of the complex-shaped models of Al-SiC. Three different volume fractions of SiC particles, precisely 10%, 15%, and 25%, are investigated in a composite under uniaxial tensile loading. The tensile behavior of Al-SiC composites is evaluated under two loading directions, considering both cases with and without diffusion effects. The results show that diffusion increases the ultimate tensile strength of the Al-SiC composite, particularly for the 15% SiC volume fraction. Regarding the shape of the SiC particles considered in this research, the strength of the composite varies in different directions. Specifically, the ultimate strength of the Al-SiC composite with 25% SiC reached 11.29 GPa in one direction, and 6.63 GPa in another, demonstrating the material's anisotropic mechanical behavior when diffusion effects are considered. Young's modulus shows negligible change in the presence of diffusion. Furthermore, diffusion improves toughness in Al-SiC composites, resulting in higher values compared to those without diffusion, as evidenced by the 25% SiC volume fraction composite (2.086 GPa) versus 15% (0.863 GPa) and 10% (1.296 GPa) SiC volume fractions.