Instant and Multifunctional Nanofibers Loaded with Proanthocyanidins and Hyaluronic Acid for Skincare Applications.

Hyaluronic-acid- and silk-fibroin-based nanofibrous mats loaded with proanthocyanidins and collagen peptides were fabricated as multifunctional facial masks using electrospinning. Their morphology, hygroscopicity and moisture retention, DPPH, ABTS free radical scavenging abilities, and cytocompatibility were investigated. The results showed that the nanofibrous mats were dense and uniform, with an average diameter ranging from 300 to 370 nm. The nanofibrous mats exhibited satisfactory moisture retention, oxidation resistance, biocompatibility, especially excellent DPPH, and ABTS free radical scavenging capacities. DPPH free radical scavenging activity was 90% with 15 mg/L nanofibers, and ABTS free radical scavenging activity was 90% with 0.005 mg/L nanofibers. The nanofibrous mats protected fibroblasts from oxidative stress damage induced by tert-butyl hydroperoxide (t-BHP) and significantly promoted their proliferation. Compared with traditional liquid masks and semi-solid facial masks, the multifunctional nanofibrous mats prepared in this study contained fewer additives, which has significant advantages in terms of safety. The nanofibrous mats were rapidly dissolved within 5 s after being sprayed with water, which facilitated the release and penetration of active ingredients for skincare. Therefore, the multifunctional nanofibrous mats displayed excellent moisture retention, oxidation resistance, and biocompatibility, indicating promising translational potential as facial masks and providing a valuable reference for skincare.