Mechanical strength of stock and custom abutments as original and aftermarket components after thermomechanical aging.
Article in Clinical and experimental dental research, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Fatigue Resistance of Customized Implant-Supported Restorations.Materials (Basel, Switzerland) · 2025Article
- Mechanical strength of stock and custom abutments as original and aftermarket components after thermomechanical aging.Clinical and experimental dental research · 2024Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
objectivesThe study aimed to assess the impact on the mechanical strength and failure patterns of implant-abutment complexes of choosing different abutment types, designs and manufacturers, aiding in selecting the optimal restorative solution. Stock and custom abutments from original and aftermarket suppliers were subjected to thermomechanical aging. MATERIAL AND
methodsStock and custom abutments from the implant manufacturer (original) and a aftermarket supplier (nonoriginal) were connected to identical implants with internal connection. Custom abutments were designed in a typical molar and premolar design, manufactured using the workflow from the respective suppliers. A total of 90 implants (4 mm diameter, 3.4 mm platform, 13 mm length) equally divided across 6 groups (three designs, two manufacturers) underwent thermo-mechanical aging according to three different regimes, simulating five (n = 30) or 10 years (n = 30) of clinical function, or unaged control (n = 30). Subsequently, all samples were tested to failure.
resultsDuring aging, no failures occurred. The mean strength at failure was 1009N ± 171, showing significant differences between original and nonoriginal abutments overall (-230N ± 27.1, p < .001), and within each abutment type (p = .000), favoring original abutments. Aging did not significantly affect the failure load, while the type of abutment and manufacturer did, favoring original and custom-designed abutments. The most common failure was implant bending or deformation, significantly differing between original and nonoriginal abutments and screws. All failure tests resulted in clinically unsalvageable implants and abutments.
conclusionsWithin the limitations of this study, original abutments exhibited a higher mechanical strength compared to the nonoriginal alternative, regardless of the amount of simulated clinical use. Similarly, custom abutments showed higher mechanical strength compared to stock abutments. However, mechanical strength in all abutments tested was higher than average chewing forces reported in literature, thus components tested in this study can be expected to perform equally well in clinical situations without excessive force.