Assessment of Environmental Impact on Glass-Fiber-Reinforced Polymer Pipes Mechanical and Thermal Properties.
Article in Polymers, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed.
- Experimental Assessment of Stress-Strain Response in Filament-Wound GFRP Pipes Under Internal Pressure Loading.Materials (Basel, Switzerland) · 2026Article
- Hardness and Roughness of Glass/Epoxy Composite Laminates Subjected to Different Hostile Solutions: A Comparative Study.Polymers · 2025Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
8 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Glass-fiber-reinforced polymer (GFRP) composites are widely used due to their high strength-to-weight ratio and corrosion resistance. However, their properties can degrade under different environmental conditions, affecting long-term reliability. This study examines the effects of temperature and chemical environments on GFRP pipes. Specimens were exposed to salt water and alkaline solutions at 20 °C and 50 °C. Diffusion coefficients and tensile and flexural properties were measured. Advanced techniques (TGA, FT-IR, and XRD) showed a 54.73% crystallinity difference between samples at 20 °C/air and 50 °C/salt water. Elevated temperatures and alkaline conditions accelerated degradation, with diffusion coefficients 68.38% higher at 50 °C/salt water compared to at 20 °C/salt water. Flexural strength decreased by 47.65% and tensile strength by 13.89%, at 50 °C/alkaline compared to 20 °C/air. Temperature was identified as the primary factor affecting mechanical performance, while alkaline environments significantly influenced tensile and flexural modulus. These results underscore the importance of considering environmental factors for the durability of GFRP composites.