New Fire-Retardant Open-Cell Composite Polyurethane Foams Based on Triphenyl Phosphate and Natural Nanoscale Additives.

Despite the mechanical and physical properties of polyurethane foams (PUF), their application is still hindered by high inflammability. The elaboration of effective, low-cost, and environmentally friendly fire retardants remains a pressing issue that must be addressed. This work aims to show the feasibility of the successful application of natural nanomaterials, such as halloysite nanotubes and nanocellulose, as promising additives to the commercial halogen-free, fire-retardant triphenyl phosphate (TPP) to enhance the flame retardance of open-cell polyurethane foams. The nanocomposite foams were synthesized by in situ polymerization. Investigation of the mechanical properties of the nanocomposite PUF revealed that the nanoscale additives led to a notable decrease in the foam's compressibility. The obtained results of the flammability tests clearly indicate that there is a prominent synergetic effect between the fire-retardant and the natural nanoscale additives. The nanocomposite foams containing a mixture of TPP (10 and 20 parts per hundred polyol by weight) and either 10 wt.% of nanocellulose or 20 wt.% of halloysite demonstrated the lowest burning rate without dripping and were rated as HB materials according to UL 94 classification.