An in vitro evaluation of the fatigue behavior of resin composite materials as part of a translational research cycle.
Article in Dental materials : official publication of the Academy of Dental Materials, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 3 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
3 citing papers in PubMed.
- Review
- Article
- Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
Abstract
purposeThis study aimed to reproduce and translate clinical presentations in an in vitro set-up and evaluate laboratory outcomes of mechanical properties (flexural strength, fatigue resistance, wear resistance) and link them to the clinical outcomes of the employed materials in the Radboud Tooth Wear Project (RTWP). MATERIALS AND
methodsFour dental resin composites were selected. 30 discs (Ø12.0 mm, 1.2 mm thick) were fabricated for each of Clearfil TM AP-X (AP), Filtek TM Supreme XTE (FS), Estenia TM C&B (ES), and Lava Ultimate (LU). Cyclic loading (200 N, 2 Hz frequency) was applied concentrically to 15 specimens per group with a spherical steatite indenter (r = 3.18 mm) in water in a contact-load-slide-liftoff motion (105 cycles). The wear scar was analysed using profilometry and the volume loss was digitally computed. Finally, all specimens were loaded (fatigued specimens with their worn surface loaded in tension) until fracture in a biaxial flexure apparatus. The differences in volume loss and flexural strength were determined using regression analysis.
resultsCompared to AP and FS, ES and LU showed a significantly lower volume loss (p < 0.05). Non-fatigued ES specimens had a similar flexural strength compared to nonfatigued AP, while non-fatigued FS and LU specimens had a lower flexural strength (p < 0.001; 95 %CI: -80.0 - 51.8). The fatigue test resulted in a significant decrease of the flexural strength of ES specimens, only (p < 0.001; 95 %CI: -96.1 - -54.6). CLINICAL RELEVANCE: These outcomes concur with the outcomes of clinical studies on the longevity of these composites in patients with tooth wear. Therefore, the employed laboratory test seems to have the potential to test materials in a clinically relevant way.