Comparative Evaluation of the Flexural Strength of Heat-Activated Polymethyl Methacrylate Denture Base Resin With and Without 0.2% by the Weight of Silver Nanoparticles Cured by Conventional and Autoclave Methods: An In Vitro Study.
Article in Cureus, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 2 papers, 1 of them a synthesis that pooled it.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
2 citing papers in PubMed, 1 synthesis or guideline pooled it.
- Silver Nanoparticles (AgNPs) Incorporation into Polymethyl Methacrylate (PMMA) for Dental Appliance Fabrication: A Systematic Review and Meta-Analysis of Mechanical Properties.International journal of molecular sciences · 2024Pooled it
- Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
2 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
purposeHeat-activated polymethyl methacrylate (PMMA) is the most common and widely accepted denture base material. Two important drawbacks are the development of denture stomatitis and the high incidence of fracture of denture bases. The present study investigated the effect of adding 0.2% by weight of silver nanoparticles (AgNps) and using the autoclave method of terminal boiling on the flexural strength of heat-activated PMMA denture base resin.
methodsA total of 40 samples of heat-activated PMMA blocks were divided into four groups, with 10 samples (n = 10) in each group. Group 1 consisted of unmodified heat-activated PMMA resin (PMMA-1) polymerized by the conventional method of terminal boiling (conventional curing); Group 2 consisted of 0.2% by weight AgNPs added to heat-activated PMMA resin (PMMA-2) polymerized by conventional curing; Group 3 consisted of PMMA-1 polymerized by the autoclave method of terminal boiling (autoclave curing); and Group 4 consisted of PMMA-2 polymerized by autoclave curing. The flexural strength was tested using a universal testing machine. Descriptive statistics were expressed as mean ± SD and median flexural strength. Kruskal-Wallis ANOVA with Mann-Whitney U post hoc test was applied to test for statistical significance between the groups. The level of significance was set at p<0.05.
resultsThe results showed a statistically significant reduction in flexural strength in Group 2 compared to Group 1. The samples from Group 4 showed a statistically significant increase in flexural strength compared to Group 2. The Group 4 denture base had the highest flexural strength (115.72 ± 7.27 MPa) among the four groups, followed by Group 3 (104.16 ± 4.85 MPa). The Group 1 samples gave a flexural strength of 101.45 ± 3.13 MPa, and Group 2 gave the lowest flexural strength (85.98 ± 3.49 MPa) among the four groups tested.
conclusionThe reduction in flexural strength of the heat-activated PMMA denture base after adding 0.2% by weight of AgNP as an antifungal agent was a major concern among manufacturers of commercially available denture base materials. It was proved in the present study that employing the autoclave curing method of terminal boiling for the polymerization of 0.2% by weight of AgNp-added heat-activated PMMA denture base resulted in a significantly higher flexural strength compared to the conventional curing method of terminal boiling for polymerization. Unmodified heat-activated PMMA gave higher flexural strength values when polymerized by autoclave curing compared to the conventional curing method of terminal boiling.