Preparation and Properties of PA10T/PPO Blends Compatibilized with SEBS-g-MAH.

Plant-derived PA10T is regarded as one of the most promising semi-aromatic polyamides; however, shortcomings, including low dimensional accuracy, high moisture absorption, and relatively high dielectric constant and loss, have impeded its extensive utilization. Polymer blending is a versatile and cost-effective method to fabricate new polymeric materials with excellent comprehensive performance. In this study, various ratios of PA10T/PPO blends were fabricated via melt blending with the addition of a SEBS-g-MAH compatibilizer. Molau test and scanning electron microscopy (SEM) were employed to study the influence of SEBS-g-MAH on the compatibility of PA10T and PPO. These studies indicated that SEBS-g-MAH effectively refines the domain size of the dispersed PPO phase and improves the dispersion stability of PPO particles within a hexafluoroisopropanol solvent. This result was attributed to the in situ formation of the SEBS-g-PA10T copolymer, which serves as a compatibilizer. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) results showed that the melting-crystallization behavior and thermal stability of blends closely resembled that of pure PA10T. Dynamic mechanical analysis (DMA) revealed that as the PPO content increased, there was a decrease in the glass transition temperature and storage modulus of PA10T. The water absorption rate, injection molding shrinkage, dielectric properties, and mechanical strength of blends were also systematically investigated. As the PPO content increased from 10% to 40%, the dielectric loss at 2.5 GHz decreased significantly from 0.00866 to 0.00572, while the notched Izod impact strength increased from 7.9 kJ/m