Three-Dimensional Printing of Lignocellulose Structures: Improving Mechanical Properties and Shape Fidelity.
Article in ACS omega, 2024. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Additive manufacturing of cellulose-based photopolymerizable resin with high strength and shape-memory.Nature communications · 2026Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
3 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
Additive manufacturing of nanocellulose (NC) materials is an emergent technological domain that facilitates the fabrication of complex and environment-friendly structures that mitigate greenhouse gas emissions. However, printing high concentrations of NC into intricate structures encounters substantial challenges due to inadequate adhesion between the printed layers attributed to a high cellulose solid content, resulting in low shape fidelity and mechanical properties. Therefore, to address these challenges, this paper reports lignin (LG) blending, a nanofiller, in high-content NC (>25 wt % solid content) paste to improve the layer adhesion of three-dimensional (3D) printed structures. The printed structures are dried in a clean room condition followed by postcuring. The optimized lignocellulose (0.5LG-NC) paste showed high structural shape fidelity, remarkable flexural strength, and moduli of 102.93 ± 0.96 MPa and 9.05 ± 0.07 GPa. Furthermore, the volumetric shrinkage behavior in box-like 3D printed structures with optimized LG-NC paste shows low standard deviations, demonstrating the repeatability of the printed structures. The study can be adapted for high-performance engineering and biomedical applications to manufacture high mechanical strength environment-friendly structures.