On the Ion Implantation Synthesis of Ag-Embedded Over Sr-Substituted Hydroxyapatite on a Nano-Topography Patterned Ti for Application in Acetabular Fracture Sites.

Introduction: There is an ongoing need for improved healing response and expedited osseointegration on the Ti implants in acetabular fracture sites. To achieve adequate bonding and mechanical stability between the implant surface and the acetabular fracture, a new coating technology must be developed to promote bone integration and prevent bacterial growth. Methods: A cylindrical Ti substrate mounted on a rotating specimen holder was used to implant Ca Results: The properties of the as-formed ion-implanted specimen were compared with the SrHA-Ag synthesized specimens by cathodic deposition and low-temperature high-speed collision technique. The adhesion strength of the ion-implanted specimen was 43 ± 2.3 MPa, which is well above the ASTM standard for Ca-P coating on Ti. Live/dead cell analysis showed higher osteoblast activity on the ion-implanted specimen than the other two. Ag in the SrHA implanted Ti by ion implantation process showed superior antibacterial activity. Discussion: In the ion implantation technique, nano-topography patterned surfaces are not concealed after implantation, and their efficacy in interacting with the osteoblasts is retained. Although all three studies examined the antibacterial effects of Ag